C34500 High Leaded Brass

C34500 high leaded brass "64%" is the brass with high machining ability. The increase in lead content will result in increased machining ability with good strength and atmospheric corrosion resistance. The increased lead content will also provide pressure tightness by sealing the shrinkage pores.

Applications:

Industrial: Pinions, Gears, Valve Stems, Flare Fittings, Adapters, Couplings

Plumbing: Plumbing Fittings, Plumbers' Brass Goods

Equivalent Specifications:

Specifications	Designation
BS	CZ131 / CZ119
EN	CW601N/CuZn35Pb2
JIS	C3560
DIN	2.0331
ISO	-
Russian (GOST)	-

Chemical Composition:

-	Cu	Pb	Zn	Fe
Min/Max	62 - 65	1.5 – 2.5	Rem. (Max.)	0.15 (Max.)

Physical Properties:

Melting Point – Liquids °F	1670
Melting Point – Solidus °F	1630
Density lb/cu in. at 68 °F	0.306
Specific Gravity	8.47
Electrical Conductivity %IACS at 68°F	26
Thermal Conductivity Btu/ sq ft/ ft hr/ F at 68°F	67
Coefficient of Thermal Expansion 68-572 10?6 per °F (68 – 572°F)	11.3
Specific Heat Capacity Btu/ lb /°F at 68°F	0.09
Modulus of Elasticity in Tension ksi	15000
Modulus of Rigidity ksi	5600

Mechanical Properties:

Form	Temper Code	Tensile Strength (ksi)	YS-0.5% Ext (ksi)	Elongation (%)	Rockwell B Scale	Section Size (in)
Rods	H02	50 Min for Standard 62 Max for Standard	20 Min for Standard	15 Min for Standard	55 Min for Standard 75 Max for Standard	0.75
	H02	57 Min for Standard 80 Max for Standard	25 Min for Standard	7 Min for Standard		<0.50

 

 