C35300 High Leaded Brass
The C35300 Thread Rolling Brass is prepared using the inexpensive thread rolling method and is mainly used for cold forging processes. It is prepared in smooth and long threads and is smooth in finish.
Product Specification
| Copper Min/Max | 60.0-63.0 |
| Diameter | 6mm - 250mm |
| Lead (Min/Max) | 1.5-2.5 |
| Ferrum (Min/Max) | .15 |
| Minimum Order Quantity | 1000 Kilogram |
Product Description
The C35300 Thread Rolling Brass is prepared using the inexpensive thread rolling method and is mainly used for cold forging processes. It is prepared in smooth and long threads and is smooth in finish.
Applications:
Builders Hardware: Drawer Pulls, Hinges, Drawer Handles
Consumer: Bicycle Spoke Nipples, Clock and Watch Parts, Clock Plates and Nuts, Key Blanks
Fasteners: Nuts, Rivets, Screws
Industrial: Ratchets, Instrument Backs, Automatic Screw Machine Parts, Valve Stems, Pinions, Flare Fittings, Couplings, Bearing Cages, Channel Plate, Wheels, Gears, Adapters, Engravers Plate
Plumbing: Faucet Seats, Faucet Stems, Pipe Fittings, Plumbers Fittings, Plumbers' Brass Goods
Technical Specifications:
| Specifications | Designation |
| ISO | CuZn37Pb2 |
| Europen | CuZn37Pb2 |
| JIS | CuZn37Pb2 |
| Russian | CZ119 |
Chemical Composition:
| Cu | Fe | Pb | Zn | |
| Min/Max | 60.0-63.0 | .15 | 1.5-2.5 | Rem |
| Nominals | 61.5 | - | 2.0 | 36.5 |
Specifications:
| End Product | Specification |
| Bar | ASTM B121 |
| Wire | ASTM B121 |
| Rod | ASTM B453 |
| Ingot | ASTM B121 |
Fabrication:
| Joining Technique | Suitability |
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Fair |
| Capacity for Being Hot Formed | Poor |
| Machinability Rating | 90 |