CAC301 to CAC304, a basic introduction to four different types of high-strength brass

CAC301 to CAC304, a basic introduction to four different types of high-strength brass

There are four types of high-strength brass models, namely: CAC301 type (original JIS symbol: HBsC1); CAC302 type (original JIS symbol: HBsC2) CAC303 type (original JIS symbol: HBsC3); CAC304 type (original JIS symbol: HBsC4) . This article describes the basic applications and properties of four high-strength brasses. Among them, CAC304 model high-strength brass is currently the most widely used one. Jiaxing Gurun can provide various types of CAC304 high-strength brass products.

1. CAC301 type (original JIS symbol: HBsC1)

It has superior strength and hardness compared to brass castings and has excellent corrosion resistance and toughness

*The following mechanical property values are general representative values, not standard values.

[Use] Ship accessories, ship propellers, bearings, levers, valve parts

[Hardness] HBW 137 (10/3000)

[Tensile strength] 450 N/mm2

[Load-bearing]140 N/m㎡

[Extension rate] 25%

[Conductivity] 22%

[Specific resistance] 7.81 microΩ/cm

[Thermal conductivity] 99 W/m

[Specific heat]0.09 calories/g (20°C)

[Density]8.3

2. CAC302 type (original JIS symbol: HBsC2)

It has better mechanical properties and better wear resistance than CAC301

*The following mechanical property values are general representative values, not standard values.

[Use] Ship propellers, bearings, end plates, general mechanical parts, special cylinder parts

【Hardness】HBW 137 (10/3000)

[Tensile strength] 430 N/mm㎡

[Load-bearing]175 N/m㎡

[Extension rate] 18%

[Conductivity] 19%

[Thermal conductivity] 88 W/m

[Specific heat]0.09 cal/g/degree Celsius (20°C)

[Density]8.2

3. CAC303 type (original JIS symbol: HBsC3)

YC (casting), YE (extruded with casting composition), YF (forged with casting composition)

Better strength, hardness and wear resistance than CAC302

*The following mechanical property values are general representative values, not standard values.

[Application] Low-speed, high-load sliding parts, large valves, hydraulic cylinders, general mechanical parts

【Hardness】HBW 167 (10/3000)

[Tensile strength] 635 N/mm2

[Load-bearing]305 N/m㎡

[Extension rate] 15%

[Conductivity] 8%

[Specific resistance] 22.7 μΩ/cm

[Thermal conductivity] 50 W/m

[Specific heat]0.09 cal/g/degree Celsius (20°C)

[Density]7.85

4. CAC304 type (original JIS symbol: HBsC4)

YC-4 (casting), YE-4 (extrusion), YF-4 (forging molding, casting composition)

Among high-strength brasses, it has the best strength and hardness, and has excellent wear resistance even under high loads.

*The following mechanical property values are general representative values, not standard values.

[Use] Low-speed, high-load sliding parts, bearings, wear-resistant plates, general mechanical parts

【Hardness】HBW 216 (10/3000)

[Tensile strength]755 N/mm㎡

[Load-bearing]410 N/m㎡

[Extension rate] 12%

[Conductivity] 8%

[Specific resistance] 21.7μΩ/cm

[Thermal conductivity] 50 W/m

[Specific heat]0.09 cal/g/degree Celsius (20°C)

[Density]7.84