CuZn35Pb2Al-C ( CC752S )
| Grade : | CuZn35Pb2Al-C |
| Number: | CC752S |
| Classification: | Copper-zinc alloy |
| Standard: | EN 1982: 2008 Copper and copper alloys. Ingots and castings |
| Equivalent grades: | No information |
Chemical composition % of grade CuZn35Pb2Al-C ( CC752S )
| A suffix -C is added to the designation to identify material in the form of castings |
| Fe | Si | Mn | Ni | Al | Cu | As | Pb | Sb | Sn | - |
| max 0.3 | max 0.02 | max 0.1 | max 0.2 | 0.3 - 0.7 | 61.5 - 64.5 | 0.04 - 0.14 | 1.5 - 2.2 | max 0.14 | max 0.3 | Zn - remainder |
Mechanical properties of grade CuZn35Pb2Al-C ( CC752S )
| Rm - Tensile strength (MPa) (GM) | 280 |
| Rp0.2 0.2% proof strength (MPa) (GM) | 120 |
| A - Min. elongation at fracture (%) (GM) | 10 |
| Brinell hardness (HBW): (GM) | 70 |
Casting process
| GS | Sand casting |
| GM | Permanent mould casting |
| GZ | Centrifugal casting |
| GC | Continuous casting |
| GP | Pressure die casting |
Material conditions
| R | Material condition designated by the minimum value of tensile strength requirement for the product with mandatory tensile strength and elongation requirements |
| H | Material condition designated by the minimum value of hardness requirement for the product with mandatory hardness requirements |
Mechanical properties
| ReH | Minimum yield strength / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Tensile strength / Zugfestigkeit / Resistance a la traction |
| A | Minimum elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Notch impact test / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn35Pb2Al-C ( CC752S ) Copper-zinc alloy |